CAST 13 | CAST 13 ES | CAST 15 | CAST 16 | CAST 16 ES | ||
---|---|---|---|---|---|---|
Maximum Service Temperature | °C | 1,300 | 1,300 | 1,500 | 1,600 | 1,600 |
Maximum Grain Size of Aggregates | mm. | 5 | 5 | 5 | 5 | 5 |
Approximate Weight Required for Casting | kg/m3 | 2,010 – 2,020 | 2,010 – 2,020 | 2,200 – 2,210 | 2,500 – 2,530 | 2,520 – 2,540 |
Approximate Amount of Water Required for Casting | % | 10 – 20 | 10 – 12 | 10 – 12 | 10 – 12 | 10 – 12 |
Bulk Density After Drying at 110°C | kg/m3 | 2,050 – 2,070 | 2,110 – 2,020 | 2,250 – 2,260 | 2,350 – 2,380 | 2,350 – 2,400 |
Cold Crushing Strength After Drying at 110°C | kg/cm2 | 350 – 380 | 400 – 450 | 300 – 320 | 380 – 400 | 400 – 450 |
Modulus of Rupture | ||||||
– After Drying at 110°C | kg/cm2 | 60 – 70 | 70 – 80 | 70 – 75 | 70 – 75 | 70 – 75 |
– After Heating at | kg/cm2 | (1,260°C) 35 – 40 | (1,480°C) 60 – 70 | (1,480°C) 80 – 85 | (1,480°C) 80 – 85 | (1,480°C) 80 – 85 |
Permanent Linear Change After Heating at | % | (1,260°C) +0.5 | (1,480°C) +0.5 | (1,480°C) -0.5 | (1,480°C) -0.15 | (1,480°C) -0.15 |
CAST 17 CG | CAST 18 | CAST 11 LW | CAST 13 LW | ||
---|---|---|---|---|---|
Maximum Service Temperature | °C | 1,700 | 1,800 | 1,100 | 1,300 |
Maximum Grain Size of Aggregates | mm. | 12.5 | 5 | 3 | 5 |
Approximate Weight Required for Casting | kg/m3 | 2,560 – 2,580 | 2,700 – 2,730 | 800 – 900 | 1,200 – 1,300 |
Approximate Amount of Water Required for Casting | % | 10 – 20 | 10 – 12 | 40 – 50 | 35 |
Bulk Density After Drying at 110°C | kg/m3 | 2,640 – 2,650 | 2,800 – 2,820 | 900 – 950 | 1,400 – 1,450 |
Cold Crushing Strength After Drying at 110°C | kg/cm2 | 380 – 400 | 490 – 500 | 30 – 40 | 110 – 120 |
Modulus of Rupture | |||||
– After Drying at 110°C | kg/cm2 | 80 – 85 | 100 – 120 | 8.0 | 20 – 25 |
– After Heating at | kg/cm2 | (1,480°C) 90 – 100 | (1,480°C) 490 – 100 | (1,000°C) 4.0 | (1,260°C) 40 – 45 |
Permanent Linear Change After Heating at | % | (1,480°C) -0.5 | (1,480°C) -0.18 | (1,000°C) -0.08 | (1,260°C) -0.05 |
C60 | C82 | ALC90 | NEO – 165 | ||
---|---|---|---|---|---|
Maximum Service Temperature | °C | 1,600 | 1,700 | 1,750 | 1,650 |
Maximum Grain Size of Aggregates | mm. | 12.5 | 12.5 | 12.5 | 12.5 |
Approximate Weight Required for Casting | kg/m3 | 2,400 – 2,430 | 2,800 – 2,850 | 3,150 – 3,200 | 2,650 |
Approximate Amount of Water Required for Casting | % | 5.0 – 5.5 | 5.0 – 5.5 | 4.0 – 4.5 | 5.0 |
Bulk Density After Drying at 110°C | kg/m3 | 2,430 – 2,440 | 2,840 – 2,860 | 3,150 | 2,760 |
Cold Crushing Strength After Drying at 110°C | kg/cm2 | 520 – 550 | 340 – 350 | 300 – 350 | 80 – 90 |
Modulus of Rupture | |||||
– After Drying at 110°C | kg/cm2 | 60 – 65 | 40 | 45 | 625 – 650 |
Permanent Linear Change After Heating at 1,400°C | % | -0.50 | -0.40 | -0.20 | -0.15 |
CAST 13 | CAST 13 ES | CAST 15 | CAST 16 | CAST 16 ES | ||
---|---|---|---|---|---|---|
Maximum Service Temperature | °C | 1,300 | 1,300 | 1,500 | 1,600 | 1,600 |
Maximum Grain Size of Aggregates | mm. | 5 | 5 | 5 | 5 | 5 |
Approximate Weight Required for Casting | kg/m3 | 2,010 – 2,020 | 2,010 – 2,020 | 2,200 – 2,210 | 2,500 – 2,530 | 2,520 – 2,540 |
Approximate Amount of Water Required for Casting | % | 10 – 20 | 10 – 12 | 10 – 12 | 10 – 12 | 10 – 12 |
Bulk Density After Drying at 110°C | kg/m3 | 2,050 – 2,070 | 2,110 – 2,020 | 2,250 – 2,260 | 2,350 – 2,380 | 2,350 – 2,400 |
Cold Crushing Strength After Drying at 110°C | kg/cm2 | 350 – 380 | 400 – 450 | 300 – 320 | 380 – 400 | 400 – 450 |
Modulus of Rupture | ||||||
– After Drying at 110°C | kg/cm2 | 60 – 70 | 70 – 80 | 70 – 75 | 70 – 75 | 70 – 75 |
– After Heating at | kg/cm2 | (1,260°C) 35 – 40 | (1,480°C) 60 – 70 | (1,480°C) 80 – 85 | (1,480°C) 80 – 85 | (1,480°C) 80 – 85 |
Permanent Linear Change After Heating at | % | (1,260°C) +0.5 | (1,480°C) +0.5 | (1,480°C) -0.5 | (1,480°C) -0.15 | (1,480°C) -0.15 |
CAST 17 CG | CAST 18 | CAST 11 LW | CAST 13 LW | ||
---|---|---|---|---|---|
Maximum Service Temperature | °C | 1,700 | 1,800 | 1,100 | 1,300 |
Maximum Grain Size of Aggregates | mm. | 12.5 | 5 | 3 | 5 |
Approximate Weight Required for Casting | kg/m3 | 2,560 – 2,580 | 2,700 – 2,730 | 800 – 900 | 1,200 – 1,300 |
Approximate Amount of Water Required for Casting | % | 10 – 20 | 10 – 12 | 40 – 50 | 35 |
Bulk Density After Drying at 110°C | kg/m3 | 2,640 – 2,650 | 2,800 – 2,820 | 900 – 950 | 1,400 – 1,450 |
Cold Crushing Strength After Drying at 110°C | kg/cm2 | 380 – 400 | 490 – 500 | 30 – 40 | 110 – 120 |
Modulus of Rupture | |||||
– After Drying at 110°C | kg/cm2 | 80 – 85 | 100 – 120 | 8.0 | 20 – 25 |
– After Heating at | kg/cm2 | (1,480°C) 90 – 100 | (1,480°C) 490 – 100 | (1,000°C) 4.0 | (1,260°C) 40 – 45 |
Permanent Linear Change After Heating at | % | (1,480°C) -0.5 | (1,480°C) -0.18 | (1,000°C) -0.08 | (1,260°C) -0.05 |
C60 | C82 | ALC90 | NEO – 165 | ||
---|---|---|---|---|---|
Maximum Service Temperature | °C | 1,600 | 1,700 | 1,750 | 1,650 |
Maximum Grain Size of Aggregates | mm. | 12.5 | 12.5 | 12.5 | 12.5 |
Approximate Weight Required for Casting | kg/m3 | 2,400 – 2,430 | 2,800 – 2,850 | 3,150 – 3,200 | 2,650 |
Approximate Amount of Water Required for Casting | % | 5.0 – 5.5 | 5.0 – 5.5 | 4.0 – 4.5 | 5.0 |
Bulk Density After Drying at 110°C | kg/m3 | 2,430 – 2,440 | 2,840 – 2,860 | 3,150 | 2,760 |
Cold Crushing Strength After Drying at 110°C | kg/cm2 | 520 – 550 | 340 – 350 | 300 – 350 | 80 – 90 |
Modulus of Rupture | |||||
– After Drying at 110°C | kg/cm2 | 60 – 65 | 40 | 45 | 625 – 650 |
Permanent Linear Change After Heating at 1,400°C | % | -0.50 | -0.40 | -0.20 | -0.15 |